Resistance welding is best suited for welding the quality., Brass round material 2., 0401 Ms58 has relatively low corrosion resistance. In particular, it is not resistant to various salt solutions, organic liquids and water. Brass round rod with the material number 2.0401 consists of copper (about 57-59%), lead (about 2.5-3.5%) and a rest of zinc (approx. 36-40%) together. The material 2.0401 is well warm moldable, but high hardness and strength of quality are achieved by cold formability Brass round material also has very good machinability and is suitable for soft and brazing soldering. Brass rod (Ms58 / 2., 0401) rod round rod solid rod round material Description: Brass round rod with the material number 2., 0401 is made of copper (about 57-59%), lead (about 2., 5-3., 5%) and a rest of zinc (approx., 36-40%) together., The material 2., 0401 is easily heat formable, but high hardness and strength of the quality are achieved by cold formability. Carbon Steel Solid 16 mm Iron Rod Carbon Round Steel Bar - Round Bar Stainless Steel Rod Round Bar Rod 6mm x 600mm Due to the lead content, brass round steel can only be welded. The material must not be welded using the following welding processes: Arc hand welding, gas welding, TIG and MIG welding. Properties: very good heat-formability; very good machinability; suitable for soft and brazing; well punched and mechanically polished; only partially weldable (resistance welding best recommended); relatively low corrosion resistance to aggressive media (water, various salt solutions and organic liquids)., Density — 8., 47 kg/dm³; thermal conductivity — 123 W/m·K electric., Resistance — 0., 066 mm²/m Electric Conductivity — 15m/Ωmm²; Melting point — 888°C; Tensile strength — Min., 360MPa; Brass Rods For Modelling Brass Round Bar 2.0401 75 Mm Ms58 Round Disc 0.5 M CuZn39Pb3 Brass Material Length tolerance +/-2 mm